Weak Localization in Polycrystalline Tin Dioxide Films
The electrical and magnetotransport properties of nanocrystalline tin dioxide films were studied in the temperature range of 4–300 K and in magnetic fields up to 8 T. SnO<sub>2−δ</sub> films were fabricated by reactive direct current (DC) magnetron sputtering of a tin target with followi...