The effect of molten salt on the mechanical properties and microstructure of CuNiSi alloys with reinforced Fe
In this study, CuNiSi alloys were produced using powder metallurgy in molten salt (KBr). In the Cu, Ni, and Si powder mixture, Fe was added at a rate of 2.5%, 5 and 7.5% and mechanical alloying was carried out for 4 hours at 400 rpm. Prepared powder mixtures were cold pressed under 600 MPa pressure...