The effect of porosity and cu rate on microstructure and mechanical properties of co alternative powder metallurgy compound
Cu-Ni-MX1480 powder compound were prepared at six different alloy ratios and cold pressed with a pressure of 300 MPa. Then 12 samples were obtained by hot pressing at 700 оC with 20 MPa pressure and at 800°C with 30 MPa pressure for 4 minutes in a vacuum atmosphere hot pressing machine. Por...