Compressive Deformation Behavior of an Ultrafine/Nano Grained AZ31 Magnesium Processed by Accumulative Back Extrusion
An AZ31magneium alloy was processed through accumulative back extrusion (ABE) process at 280 °C up to six passes. Compressive deformation behavior of the processed materials was studied by employing uniaxial compression tests at room temperature. The results indicated that grains of 80 nm to 1 µm si...
Main Authors: | Fatemi S.M., Zarei-Hanzaki A., Paul H. |
---|---|
Format: | Article |
Language: | English |
Published: |
Polish Academy of Sciences
2016-09-01
|
Series: | Archives of Metallurgy and Materials |
Online Access: | http://www.degruyter.com/view/j/amm.2016.61.issue-3/amm-2016-0260/amm-2016-0260.xml?format=INT |
Similar Items
-
Mechanical Behavior of an Ultrafine/Nano Grained Magnesium Alloy
by: Seyed Mahmood Fatemi, et al.
Published: (2017-06-01) -
Mechanism of plasticity enhancement of AZ31B magnesium alloy sheet by accumulative alternating back extrusion
by: Ye Wang, et al.
Published: (2023-05-01) -
Anisotropy in dynamic recrystallization behavior of AZ31 magnesium alloy
by: S.M. Fatemi, et al.
Published: (2022-12-01) -
Formation of ultrafine grains in magnesium alloy during dynamic extrusion at room temperature
by: Tao Wang, et al.
Published: (2022-09-01) -
Numerical Simulation and Experiment Study on Extrusion of AZ31 Magnesium Alloy Tube
by: SUN Ying-di, et al.
Published: (2017-06-01)