Effect of microstructure changes on magnetic properties of spark plasma sintered Nd-Fe-B powders
In this study the SPS method was applied for low RE content (8,5% at.) and high RE content (13,5 % at.) MQ powders. The powders were sintered in a wide range of temperature, for 5 min., under pressure of 35 MPa. The low RE content grade, densified reluctantly and gained the density close to the theo...