Corrosion Behaviour of Mg98.5Nd1Zn0.5 (at. %) Alloy in Phosphate Buffered Saline Solution
The corrosion behaviour of Mg98.5-Nd1-Zn0.5 (at. %) alloy was studied in phosphate buffered saline (PBS) solution to evaluate its degradation performance as a potential candidate for biomedical applications. The alloy, produced by casting and hot extrusion, consists of a fine-grained magnesium matri...