Corrosion Behaviour of Mg98.5Nd1Zn0.5 (at. %) Alloy in Phosphate Buffered Saline Solution
The corrosion behaviour of Mg98.5-Nd1-Zn0.5 (at. %) alloy was studied in phosphate buffered saline (PBS) solution to evaluate its degradation performance as a potential candidate for biomedical applications. The alloy, produced by casting and hot extrusion, consists of a fine-grained magnesium matri...
Main Authors: | Sandra Cabeza, Pablo Pérez Zubiaur, Gerardo Garcés, Carmen Andrade, Paloma Adeva |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-01-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/10/1/148 |
Similar Items
-
Influence of Ce micro-alloying on the microstructure and corrosion behavior of sub-rapid solidified Mg-4.5Al-1.5Sn-0.5Ca alloys
by: Zhong-Zheng Jin, et al.
Published: (2023-09-01) -
Microstructure and mechanical properties of the Mg98.5Zn0.5RE1 (RE=Gd and/or Y) alloys processed by equal channel angular pressing
by: Xiaojie Zhou, et al.
Published: (2023-09-01) -
Individual effect of Y and Nd on the microstructure formation of Mg-Y-Nd alloys processed by severe plastic deformation and their effect on the subsequent mechanical and corrosion properties
by: Mária Zemková, et al.
Published: (2023-02-01) -
Stress corrosion cracking susceptibility of a high strength Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy
by: S.D. Wang, et al.
Published: (2014-12-01) -
High cycle fatigue behavior of the forged Mg–7Gd–5Y–1Nd–0.5Zr alloy
by: D. Wu, et al.
Published: (2014-12-01)