The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders
In this study, 4.5 wt. %Cu powder was added to Al powder and mixed for 45 minutes to produce premixed metal powders. Premixed powders were compacted by cold pressing at 20 MPa. After that these samples were pressed at 500℃ under 200 MPa for 30 minutes by hot pressed method. Hot pressed block sample...