The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders
In this study, 4.5 wt. %Cu powder was added to Al powder and mixed for 45 minutes to produce premixed metal powders. Premixed powders were compacted by cold pressing at 20 MPa. After that these samples were pressed at 500℃ under 200 MPa for 30 minutes by hot pressed method. Hot pressed block sample...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gazi University
2018-06-01
|
| Series: | Gazi Üniversitesi Fen Bilimleri Dergisi |
| Subjects: | |
| Online Access: | http://dergipark.gov.tr/download/article-file/435035 |
| _version_ | 1797909255373717504 |
|---|---|
| author | Kübra KÖPRÜLÜ Nefise MUTLU Adem KURT Behçet GÜLENÇ Yusuf ÖZÇATALBAŞ |
| author_facet | Kübra KÖPRÜLÜ Nefise MUTLU Adem KURT Behçet GÜLENÇ Yusuf ÖZÇATALBAŞ |
| author_sort | Kübra KÖPRÜLÜ |
| collection | DOAJ |
| description | In this study, 4.5 wt. %Cu powder was added to Al powder and mixed for 45 minutes to produce premixed metal powders. Premixed powders were compacted by cold pressing at 20
MPa. After that these samples were pressed at 500℃ under 200 MPa for 30 minutes by hot pressed method. Hot pressed block samples were subjected to diffusion annealing at 540 ℃ for 2, 4, 8, 16, 32 hours. These samples, produced by powder metallurgy, are used at metallographic and microscopic researches to investigate the diffusion process. During the diffusion annealing, it was determined that significant amount of copper powder particles was dissolved in the Al matrix by diffusion. Diffusion annealing was followed by aging heat treatment, characterized by metallographic and mechanical tests. According to the increasing
the annealing time, the homogeneity of the chemical composition is not provided, however the increasing of the heat treatment (T6) capability of the produced parts, and partial porosity which
is believed to be due to atomic diffusion, have been observed. |
| first_indexed | 2024-04-10T11:05:29Z |
| format | Article |
| id | doaj.art-5c4a8cb2eacc4e3f8d468156663536c8 |
| institution | Directory Open Access Journal |
| issn | 2147-9526 2147-9526 |
| language | English |
| last_indexed | 2024-04-10T11:05:29Z |
| publishDate | 2018-06-01 |
| publisher | Gazi University |
| record_format | Article |
| series | Gazi Üniversitesi Fen Bilimleri Dergisi |
| spelling | doaj.art-5c4a8cb2eacc4e3f8d468156663536c82023-02-15T16:19:23ZengGazi UniversityGazi Üniversitesi Fen Bilimleri Dergisi2147-95262147-95262018-06-0162283293The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu PowdersKübra KÖPRÜLÜNefise MUTLUAdem KURTBehçet GÜLENÇYusuf ÖZÇATALBAŞIn this study, 4.5 wt. %Cu powder was added to Al powder and mixed for 45 minutes to produce premixed metal powders. Premixed powders were compacted by cold pressing at 20 MPa. After that these samples were pressed at 500℃ under 200 MPa for 30 minutes by hot pressed method. Hot pressed block samples were subjected to diffusion annealing at 540 ℃ for 2, 4, 8, 16, 32 hours. These samples, produced by powder metallurgy, are used at metallographic and microscopic researches to investigate the diffusion process. During the diffusion annealing, it was determined that significant amount of copper powder particles was dissolved in the Al matrix by diffusion. Diffusion annealing was followed by aging heat treatment, characterized by metallographic and mechanical tests. According to the increasing the annealing time, the homogeneity of the chemical composition is not provided, however the increasing of the heat treatment (T6) capability of the produced parts, and partial porosity which is believed to be due to atomic diffusion, have been observed.http://dergipark.gov.tr/download/article-file/435035Al-CuPowder MetallurgyPre-mixed PowderAlloyingArtificial ageing |
| spellingShingle | Kübra KÖPRÜLÜ Nefise MUTLU Adem KURT Behçet GÜLENÇ Yusuf ÖZÇATALBAŞ The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders Gazi Üniversitesi Fen Bilimleri Dergisi Al-Cu Powder Metallurgy Pre-mixed Powder Alloying Artificial ageing |
| title | The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders |
| title_full | The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders |
| title_fullStr | The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders |
| title_full_unstemmed | The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders |
| title_short | The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders |
| title_sort | effect of heat treatments on alloying of pre mixed al 4 5 wt cu powders |
| topic | Al-Cu Powder Metallurgy Pre-mixed Powder Alloying Artificial ageing |
| url | http://dergipark.gov.tr/download/article-file/435035 |
| work_keys_str_mv | AT kubrakoprulu theeffectofheattreatmentsonalloyingofpremixedal45wtcupowders AT nefisemutlu theeffectofheattreatmentsonalloyingofpremixedal45wtcupowders AT ademkurt theeffectofheattreatmentsonalloyingofpremixedal45wtcupowders AT behcetgulenc theeffectofheattreatmentsonalloyingofpremixedal45wtcupowders AT yusufozcatalbas theeffectofheattreatmentsonalloyingofpremixedal45wtcupowders AT kubrakoprulu effectofheattreatmentsonalloyingofpremixedal45wtcupowders AT nefisemutlu effectofheattreatmentsonalloyingofpremixedal45wtcupowders AT ademkurt effectofheattreatmentsonalloyingofpremixedal45wtcupowders AT behcetgulenc effectofheattreatmentsonalloyingofpremixedal45wtcupowders AT yusufozcatalbas effectofheattreatmentsonalloyingofpremixedal45wtcupowders |