The Effect of Heat Treatments on Alloying of Pre-mixed Al + 4.5 wt. %Cu Powders
In this study, 4.5 wt. %Cu powder was added to Al powder and mixed for 45 minutes to produce premixed metal powders. Premixed powders were compacted by cold pressing at 20 MPa. After that these samples were pressed at 500℃ under 200 MPa for 30 minutes by hot pressed method. Hot pressed block sample...
Main Authors: | Kübra KÖPRÜLÜ, Nefise MUTLU, Adem KURT, Behçet GÜLENÇ, Yusuf ÖZÇATALBAŞ |
---|---|
Format: | Article |
Language: | English |
Published: |
Gazi University
2018-06-01
|
Series: | Gazi Üniversitesi Fen Bilimleri Dergisi |
Subjects: | |
Online Access: | http://dergipark.gov.tr/download/article-file/435035 |
Similar Items
-
Effect of Mn on microstructure and properties of Cu-12Al powder metallurgy alloy
by: Guofei Zhang, et al.
Published: (2020-01-01) -
Mathematical relations in particulate materials processing : ceramics, powder metals, cermets, carbides, hard materials, and minerals /
by: 388326 German, Randall M., et al.
Published: (2008) -
Powder metallurgy
by: Metals Society (London)
Published: (1958) -
Powder technology and application /
by: Gai, Guosheng
Published: (2009) -
Advanced powder technology VI : selected, peer review papers from the Sixth International Latin American Conference on Powder Technology PTECH2007 /
by: International Latin-American Conference on Powder Technology (6th : 2007 : Buzios, Rio de Janeiro, Brazil), et al.
Published: (2008)