Self-Consolidation Mechanism Of Porous Ti-6Al-4V Implant Prototypes Produced By Electro-Discharge-Sintering Of Spherical Ti-6Al-4V Powders
Electro-Discharge-Sintering (EDS) was employed to fabricate Ti-6Al-4V porous implant prototypes from atomized powders (100 – 150 μm), that were subjected to discharges of 0.75 to 2.0 kJ/0.7g-powder from 150, 300, and 450 μF capacitors. Both fully porous and porous-surfaced Ti-6Al-4V compacts with va...