Ceramics Based on Sodium Rhenanite CaNaPO<sub>4</sub>, Obtained via Firing of Composite Cement-Salt Stone

Ceramics Based on Sodium Rhenanite CaNaPO<sub>4</sub>, Obtained via Firing of Composite Cement-Salt Stone

Ceramics based on rhenanite CaNaPO<sub>4</sub> with density of 0.94 g/cm<sup>3</sup> and compressive strength of 10.3 MPa was obtained via firing at 900 °C of composite cement-salt stone prepared from a hardening powder mixture of calcium citrate tetrahydrate Ca<sub>3&l...