Optimizing Heat Treatment to Improve the Microstructures and Mechanical Properties of 5CrNiMoV Steel
A strategy combining intercritical quenching, pre-tempering, and tempering processes was implemented to optimize the microstructures and mechanical properties of 5CrNiMoV steel. By intercritically quenching at 1050 °C, pr-tempering at 600 °C, and tempering at 550 °C, the steel exhibited a comprehens...