Analysis of Failure Causes of 0Cr19Ni9 Blade Crack
In this paper, fracture morphology observation, microstructure analysis, standard corrosion test, and other experimental methods are used to analyze the causes of corrosion and cracking of steam turbine blades (0Cr19Ni9) produced by a certain company. The results showed that cracks appeared during t...