Scaling of damage mechanism for additively manufactured alloys at very high cycle fatigue
Abstract A comparative analysis of fracture mechanisms in high- and very high- cycle fatigue (HCF, VHCF) regimes was carried out based on the results of multifractal analysis of the fracture surfaces of additively manufactured 316L stainless steel samples. In terms of scale invariants, the morpholog...