Formation Mechanism of MgO Containing Inclusions in the Molten Steel Refined in MgO Refractory Crucibles
In order to study the influence of MgO refractory on inclusions during the steelmaking process, laboratory quasi-equilibrium experiments were performed in MgO crucibles at 1873 K. It was found that there were no MgO-containing inclusions formed when ultra-low Al ultra-low C steel was used. When the...