Stoichiometric Cr2AlC MAX phase coatings deposited by HPPMS from composite targets using industrial deposition technology
Compositionally-graded Cr2AlC coatings were deposited from composite targets with Al concentration gradients along the long-axis of the targets, ranging from 20.0 to 30.0 at.%, in an industrial plant. Stoichiometric Cr2AlC coatings deposited by HPPMS with a peak-power density of 217 W/cm2 and at sub...