Corrosion Mechanism of L360 Pipeline Steel Coated with S8 in CO<sub>2</sub>-Cl<sup>−</sup> System at Different pH Values

Corrosion Mechanism of L360 Pipeline Steel Coated with S8 in CO<sub>2</sub>-Cl<sup>−</sup> System at Different pH Values

The corrosion behavior of L360 pipeline steel coated with or without elemental sulfur (S8) in CO<sub>2</sub>–Cl<sup>−</sup> medium at different pH was studied. An autoclave was used to simulate the working conditions for forming the corrosion scale, and an electrochemical wor...