Microstructure And Erosion-Corrosion Behaviour Of As-Cast High Chromium White Irons Containing Molybdenum In Aqueous Sulfuric-Acid Slurry
Microstructure and erosion-corrosion behaviour of as-cast high chromium white irons containing molybdenum in aqueous sulfuric-acid slurry was studied. The experimental irons contained 28 wt.%Cr with a Cr:C ratio of about 10 and up to 10 wt.%Mo. The irons with up to 6 wt.%Mo are hypoeutectic, whereas...