Influence of Martensite Deformation on Cu Precipitation Strengthening
Cu precipitation strengthening was compared in steels after treatments with and without cold rolling. A 0.2% C steel containing up to 1.5% Cu was quenched and tempered. Cu precipitation took place during tempering and increased its yield strength (YS). Quenched and tempered samples were compared wit...