An assessment of static recrystallization in L-605 Cobalt-based superalloy
In this research, the effect of cold rolling, annealing time and temperature on microstructure and hardness were studied in L-605 superalloy. A cast bar of L-605 alloy was hot rolled at 1200ºC. As the following, it was solutionized at 1230 ºC for 1 hour and finally was cold rolled by different amoun...