Phase Formation Features of Reactor Pressure Vessel Steels with Various Ni and Mn Content under Conditions of Neutron Irradiation at Increased Temperature

Phase Formation Features of Reactor Pressure Vessel Steels with Various Ni and Mn Content under Conditions of Neutron Irradiation at Increased Temperature

In this paper the phase formation and mechanical properties of VVER-type reactor pressure vessel (RPV) steels with various Ni (1.57–5.95 wt.%) and Mn (0.03–0.76 wt.%) content after neutron irradiation up to fluences in the range of (53–120) × 10<sup>22</sup> n/m<sup>2</sup> a...

Full description

Bibliographic Details
Main Authors: Evgenia Kuleshova, Ivan Fedotov, Dmitriy Maltsev, Svetlana Fedotova, Georgiy Zhuchkov, Alexander Potekhin
Format: Article
Language:English
Published: MDPI AG 2023-03-01
Series:Metals
Subjects:
reactor pressure vessel (RPV) steel
high-nickel steel
mechanical properties
phase formations
radiation embrittlement mechanisms
transmission electron microscopy