Phase evolution of matrix of C/SiCN composite during creep testing at 1300 oC
Tensile creep behavior of carbon fiber-reinforced SiCN matrix composite (C/SiCN) was investigated at 1300°C under vacuum and 45MPa for 30h. As-received and 1700°C-heat treated samples were prepared. Phase evolution and microstructure of C/SiCN was examined by virtue of X-ray diffraction, scanning el...