Microstructure and Weibull distribution of rupture strength of clay-talc ceramics
Abstract The mechanical properties of clay-talc ceramics containing 0 to 10 wt% of talc fired at 1100 °C were obtained by flexural measurements. With the average value of flexural strength of 23.1 MPa, the sample with 5 wt% of talc (G5) was the strongest and it had the lowest value of interconnected...