Graphite and Solid Fraction Evolutions during Solidification of Nodular Cast Irons
Ductile iron casting production is strongly affected by austenite and graphite distribution obtained after the solidification process. At the same time it is accepted that solidification behavior can be considered as hypo-, hyper- or eutectic depending on the chemical composition; there is still som...