Synthesis of an (Al3BC + Al2O3)/Al composite with high stiffness and attractive high-temperature tensile properties
A novel (8.5Al3BC + 14.5Al2O3)/Al composite was fabricated with exceptional elevated-temperature properties and stiffness. The composite boasts an average Young’s modulus of 99 GPa, with ultimate tensile strength and elongation of the composite at 350°C averaging 188 MPa and 4.4%, respectively. The...