Early-Stage M<sub>23</sub>C<sub>6</sub> Morphology at the Phase Boundary in Type 304L Austenitic Stainless Steel Containing δ Ferrite
The early-stage M<sub>23</sub>C<sub>6</sub> morphology at the phase boundary between austenite and δ ferrite grain in Type 304L austenitic stainless steel was investigated with transmission electron microscopy (TEM). The M<sub>23</sub>C<sub>6</sub> has...