Effect of microstructure on tensile properties of Ti-17 alloys forged using a 1500-ton forging simulator
Microstructure dependence on mechanical properties were investigated for Ti-17 forged at temperatures between 700 and 850 ˚C with deformation ratio from 33 to 80 %, and solutiontreated at 800˚C for 4 hours and aged at 620 ˚C for 8 hours. The microstructure was observed after solution and aging treat...