Microstructural Evolution of Intermetallic Compound Formed in Boron Steel Hot-Dipped in Al–7%Ni Alloy
The microstructural evolution of the intermetallic compound (IMC) layer formed on and in boron steel that was hot dipped in an Al–7Ni (wt %) bath at 690 °C for 30–180 s was investigated, and the growth mechanism of the IMC was identified. Except for the solidification structure of Al, the reaction l...