Constitutive Model and Recrystallization Mechanism of Mg-8.7Gd-4.18Y-0.42Zr Magnesium Alloy during Hot Deformation
The hot deformation behavior of Mg-8.7Gd-4.18Y-0.42Zr alloy was investigated by uniaxial hot compression tests at 300–475 °C with strain rates of 0.002–10 s<sup>−1</sup>. The average activation energy was calculated as 227.67 KJ/mol and a constitutive relation based on the Arrhenius equa...