Effect of the Initial Texture, Recrystallization and Re-Dissolution Process on the Evolution of Texture during Solution Treatment of the 7A65 Hot Rolled Plate
The evolution of textures, the degree of recrystallization and the mechanical properties of 7A65 hot rolled plates during re-dissolution were studied with different thicknesses (25 mm, 65 mm, 120 mm) and different degrees of deformation. It was found that different plates exhibited different trends...