Research on lamellar structure and micro-hardness of directionally solidified Sn-58Bi eutectic alloy
In this work, the Sn-58Bi (weight percent) eutectic alloy was directionally solidified at a constant temperature gradient (G = 12 K·mm-1) with different growth rates using a Bridgman type directional solidification furnace. A lamellar microstructure was observed in the Sn-58Bi samples. The lamellar...