Internal Crack Initiation and Growth Starting from Artificially Generated Defects in Additively Manufactured Ti6Al4V Specimen in the VHCF Regime
The aim of the present work was to investigate the ‘fine granular area’ (FGA) formation based on artificially generated internal defects in additively manufactured Ti6Al4V specimens in the early stage of fatigue crack growth in the ‘very high cycle fatigue’ (VHCF) regime. Fatigue tests were performe...