A comprehensive analysis on microstructure evolution of Mg-5.65Zn-0.66Zr alloy during hot deformation
The microstructure evolution of Mg-5.65Zn-0.66Zr (wt.%) alloy was studied based on the hot compression tests. The results indicated that the flow stress increased rapidly to a peak point at the initial stage, and then it gradually decreased. Moreover, high temperature and low strain rate resulted in...