Microstructure refinement mechanisms in undercooled solidification of binary and ternary nickel based alloys
Molten glass purification and cycle superheating technologies were used to make Ni65Cu35, Ni65Cu33Co2 and Ni65Cu31Co4 alloys obtain maximum undercoolings of 320 K, 292 K and 300 K respectively. In order to analyze the relationship between morphological characteristics of solidification front and und...