A Comparative Investigation of Mechanical Properties of TiB<sub>2</sub>/Cr Multilayer Film by Indentation
Alternating TiB<sub>2</sub>-dcMS and Cr-HiPIMS layers are used to fabricate TiB<sub>2</sub>/Cr multilayer films. Introducing a 5-nm-thick Cr interlayer deposited under a substrate bias of −60 V produces slight increases in both film hardness and elastic modulus. The TEM obser...
| Autores principales: | , , |
|---|---|
| Formato: | Artículo |
| Lenguaje: | English |
| Publicado: |
MDPI AG
2022-11-01
|
| Colección: | Magnetochemistry |
| Materias: | |
| Acceso en línea: | https://www.mdpi.com/2312-7481/8/11/148 |
| Sumario: | Alternating TiB<sub>2</sub>-dcMS and Cr-HiPIMS layers are used to fabricate TiB<sub>2</sub>/Cr multilayer films. Introducing a 5-nm-thick Cr interlayer deposited under a substrate bias of −60 V produces slight increases in both film hardness and elastic modulus. The TEM observation indicates that the Cr grains favor epitaxial growth on the TiB<sub>2</sub> interlayer, forming a coherent TiB<sub>2</sub>/Cr interface. This improves hardness. Mechanic measurement by using AFM illustrates that the coherent interface increases the elastic modulus of the Cr up to ~280 GPa, which is significantly higher than bulk material. |
|---|---|
| ISSN: | 2312-7481 |