A Comparative Investigation of Mechanical Properties of TiB<sub>2</sub>/Cr Multilayer Film by Indentation

A Comparative Investigation of Mechanical Properties of TiB<sub>2</sub>/Cr Multilayer Film by Indentation

Alternating TiB<sub>2</sub>-dcMS and Cr-HiPIMS layers are used to fabricate TiB<sub>2</sub>/Cr multilayer films. Introducing a 5-nm-thick Cr interlayer deposited under a substrate bias of −60 V produces slight increases in both film hardness and elastic modulus. The TEM obser...