A Comparative Investigation of Mechanical Properties of TiB<sub>2</sub>/Cr Multilayer Film by Indentation

A Comparative Investigation of Mechanical Properties of TiB<sub>2</sub>/Cr Multilayer Film by Indentation

Alternating TiB<sub>2</sub>-dcMS and Cr-HiPIMS layers are used to fabricate TiB<sub>2</sub>/Cr multilayer films. Introducing a 5-nm-thick Cr interlayer deposited under a substrate bias of −60 V produces slight increases in both film hardness and elastic modulus. The TEM obser...

תיאור מלא

מידע ביבליוגרפי
Main Authors: Simeng Chen, Zhengtao Wu, Qimin Wang
פורמט: Article
שפה:English
יצא לאור: MDPI AG 2022-11-01
סדרה:Magnetochemistry
נושאים:
TiB<sub>2</sub>/Cr
multilayer
mechanical properties
coherent interface
גישה מקוונת:https://www.mdpi.com/2312-7481/8/11/148