Effect of circumferential strain rate on dynamic recrystallization and texture of Mg-13Gd-4Y-2Zn-0.5Zr alloy during rotary backward extrusion
Gleeble-3500 thermal simulator was applied to realize the rotary backward extrusion forming of Mg-13Gd-4Y-2Zn-0.5Zr (wt%) alloy at different circumferential strain rate from 0.009 s−1 to 0.027 s−1 at 400 °C and the dynamic recrystallization mechanism and texture evolution were studied. The results s...