The microstructure evolution of 022Cr25Ni7Mo4N duplex stainless steel after isothermal treatment for 2-20 h at 1100℃ was studied. The morphology evolution of austenite grain was observed and the grain size was quantitatively characterized. The change of element content in austenite and ferrite phase...