Superheated Steam Treatment of Oil Palm Mesocarp Fiber Improved the Properties of Fiber-Polypropylene Biocomposite
The effect of fiber surface modification by superheated steam (SHS) treatment and fiber content (30 to 50 wt.%) was evaluated relative to the mechanical, morphology, thermal, and water absorption properties of oil palm mesocarp fiber (OPMF)/polypropylene (PP) biocomposites. SHS treatment of OPMF was...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
North Carolina State University
2016-11-01
|
| Series: | BioResources |
| Subjects: | |
| Online Access: | http://ojs.cnr.ncsu.edu/index.php/BioRes/article/view/BioRes_11_4_68_Nordin_Superheated_Steam_Treatment_Mesocarp |
| Summary: | The effect of fiber surface modification by superheated steam (SHS) treatment and fiber content (30 to 50 wt.%) was evaluated relative to the mechanical, morphology, thermal, and water absorption properties of oil palm mesocarp fiber (OPMF)/polypropylene (PP) biocomposites. SHS treatment of OPMF was conducted between 190 and 230 C for 1 h, then the SHS-treated fiber was subjected to melt-blending with PP for biocomposite production. The biocomposite prepared from SHS-OPMF treated at 210 C with 30 wt.% fiber loading resulted in SHS-OPMF/PP biocomposites with a tensile strength of 20.5 MPa, 25% higher than untreated-OPMF/PP biocomposites. A significant reduction of water absorption by 31% and an improved thermal stability by 8% at T5%degradation were also recorded. Scanning electron microscopy images of fractured SHS-OPMF/PP biocomposites exhibited less fiber pull-out, indicating that SHS treatment improved interfacial adhesion between fiber and PP. The results demonstrated SHS treatment is an effective surface modification method for biocomposite production. |
|---|---|
| ISSN: | 1930-2126 1930-2126 |