| Summary: | The objective of this study was to investigate the effects of enzymatic hydrolysis using α-amylase from <i>Bacillus amyloliquefaciens</i> on the mechanical properties of starch-based films. The process parameters of enzymatic hydrolysis and the degree of hydrolysis (DH) were optimized using a Box–Behnken design (BBD) and response surface methodology (RSM). The mechanical properties of the resulting hydrolyzed corn starch films (tensile strain at break, tensile stress at break, and Young’s modulus) were evaluated. The results showed that the optimum DH for hydrolyzed corn starch films to achieve improved mechanical properties of the film-forming solutions was achieved at a corn starch to water ratio of 1:2.8, an enzyme to substrate ratio of 357 U/g, and an incubation temperature of 48 °C. Under the optimized conditions, the hydrolyzed corn starch film had a higher water absorption index of 2.32 ± 0.112% compared to the native corn starch film (control) of 0.81 ± 0.352%. The hydrolyzed corn starch films were more transparent than the control sample, with a light transmission of 78.5 ± 0.121% per mm. Fourier-transformed infrared spectroscopy (FTIR) analysis showed that the enzymatically hydrolyzed corn starch films had a more compact and solid structure in terms of molecular bonds, and the contact angle was also higher, at 79.21 ± 0.171° for this sample. The control sample had a higher melting point than the hydrolyzed corn starch film, as indicated by the significant difference in the temperature of the first endothermic event between the two films. The atomic force microscopy (AFM) characterization of the hydrolyzed corn starch film showed intermediate surface roughness. A comparison of the data from the two samples showed that the hydrolyzed corn starch film had better mechanical properties than the control sample, with a greater change in the storage modulus over a wider temperature range and higher values for the loss modulus and tan delta, indicating that the hydrolyzed corn starch film had better energy dissipation properties, as shown by thermal analysis. The improved mechanical properties of the resulting film of hydrolyzed corn starch were attributed to the enzymatic hydrolysis process, which breaks the starch molecules into smaller units, resulting in increased chain flexibility, improved film-forming ability, and stronger intermolecular bonds.
|
|---|