Microstructure and High Temperature Deformation of Extruded Al-12Si-3Cu-Based Alloy
The high temperature deformation behavior of commercial Al-12Si-3Cu-2Ni-1Mg alloy (DM104™) which was fabricated by casting and subsequent hot extrusion was evaluated by compressive tests over the temperature range of 250–470 °C and strain rate range of 0.001–1/s. The extruded alloy had equiaxed grai...