Microstructure and Tribological Behavior of Cr-Mn-N Steel with Age-Hardened Near-Surface Layer including CrN and Fe<sub>2</sub>N Particles Intended for Use in Orthopedic Implants
This paper presents the results of a study of 17%Cr-19%Mn-0.53%N high-nitrogen austenitic stainless steel with a 25 µm thick dispersion-hardened near-surface layer intended for orthopedic applications. It was modified using a mechanical–thermal treatment (MTT) that included both friction processing...