In situ X-ray imaging of hot cracking and porosity during LPBF of Al-2139 with TiB2 additions and varied process parameters
Laser powder bed fusion (LPBF) additive manufacturing of 2XXX series Al alloys could be used for low volume specialist aerospace components, however, such alloys exhibit hot cracking susceptibility that can lead to component failure. In this study, we show two approaches to suppress the formation of...