Grain Boundary Engineering and Its Effect on Intergranular Corrosion Resistance of a Ni-Cr-Mo Based C276 Superalloy
A Ni-Cr-Mo-based C276 superalloy was cold rolled to 5–40% and annealed at 1050 °C for 30 min. The microstructure and grain boundary character distribution after cold rolling and annealing were characterized. Grain refinement and a certain amount of coincident-site lattice (CSL) boundaries were obtai...