Microstructure evolution and strengthening mechanisms of electron beam welded 2219 aluminum alloy plate after hot spinning and heat treatment
To investigate the feasibility of spinning the welded aluminum alloys, hot spinning tests were conducted on the electron beam welded (EBWed) 2219 aluminum alloy thick plates at 400 °C and successfully obtained a 2.8 mm curved welded-spun plate with a total thickness reduction of 72 %. The abnormal g...