Fabrication Technology and Material Characterization of Hot Rolled Cylindrical Fe-6.5 wt. % Si Bars

Fabrication Technology and Material Characterization of Hot Rolled Cylindrical Fe-6.5 wt. % Si Bars

Cylindrical Fe-6.5 wt. % Si bars of 7.5 mm diameter were successfully fabricated from an as-cast ingot through three rolling stages, with 10 total passes: rough rolling at 850–900 °C and 8–10 m/min; medium rolling at 800–850 °C and 10–15 m/min;...