Combined Effect of Substrate Temperature and Sputtering Power on Phase Evolution and Mechanical Properties of Ta Hard Coatings
Ta hard coatings were prepared on PCrNi1MoA steel substrates by direct current magnetron sputtering, and their growth and phase evolution could be controlled by adjusting the substrate temperature (T<sub>sub</sub>) and sputtering power (P<sub>spu</sub>) at various conditions...
Main Authors: | Cuicui Liu, Jian Peng, Zhigang Xu, Qiang Shen, Chuanbin Wang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-03-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/13/3/583 |
Similar Items
-
Comparison of CrN Coatings Prepared Using High-Power Impulse Magnetron Sputtering and Direct Current Magnetron Sputtering
by: Heda Bai, et al.
Published: (2023-09-01) -
Comparison of properties of multilayer film sputtered on glass and polypropylene substrates with angular DC magnetron Co-sputtering system
by: Preecha Changyom, et al.
Published: (2023-11-01) -
Effect of Power on Structural and Mechanical Properties of DC Magnetron Sputtered Cr Coatings
by: Wanyu Shi, et al.
Published: (2023-03-01) -
The Basic Electrochemical Properties and Structure of Direct Current Magnetron Sputtered Carbon Films
by: Zixin ZHANG, et al.
Published: (2021-03-01) -
Review of GaN Thin Film and Nanorod Growth Using Magnetron Sputter Epitaxy
by: Aditya Prabaswara, et al.
Published: (2020-04-01)