| Summary: | The aim of this study was to determine the reactivity of the chalcopyrite (112) surface under industrially relevant leaching conditions. Leaching of the chalcopyrite (112) surface was carried out at approximately pH 1 and in the presence of 0.01 M ferric or ferrous. The atomic force microscopy (AFM) and Raman microspectroscopy analyses suggested that the chalcopyrite (112) surface was relatively inert, with no formation of elemental sulfur observed over 42 days of leaching. In addition, it was found that the distribution of Fe-S and Cu-S bonds was always negatively correlated, as revealed by Raman analysis. This suggested that the breakage of the Fe-S and Cu-S bonds did not occur concurrently at a specific reaction site. The rate of variation of surface roughness, as reflected by AFM data, also suggested that leaching of the chalcopyrite (112) surface in the ferric or ferrous solution medium likely occurred more rapidly in the initial stage (fewer than seven days) than in the later stage (after seven days).
|
|---|